NYLON
|
||||||||||||
|
REINFORCED
|
SPECIALTY GRADES
|
|||||||||||
|
Grade
|
N66R-1G100
|
N66R-2G30
|
N66R-4G30
|
N66R-4G40
|
N66R-4G70
|
N66R-iGB-80
|
N66R-1M5G30
|
N66R-1M80
|
N66R-1G7TFP30
|
N66R-1M0SP0 HS
|
||
|
Property
|
Test Method
|
Measure
|
50% Fiberglass
Reinforced |
Impact Modified 15%
Fiberglass Reinforced |
High Impact
15% Fiberglass Reinforced |
High Impact
20% Fiberglass Reinforced |
High Impact
33% Fiberglass Reinforced |
40% Glass Bead
|
25% Mineral Filled
15% Fiberglass Reinforced |
40% Mineral Filled
|
33% Fiberglass
Reinforced Host Stabilized PTFE Lubricated |
MOS2 Lubricated
HSL Nylon 6/6 |
|
Melt Point
|
D-789
|
Deg F
|
490
|
490
|
255
|
509
|
.
|
.
|
.
|
490
|
.
|
489
|
|
Density
|
D-792
ISO1183 |
g/cm3
|
1.55
|
1.18
|
1.2
|
1.24
|
1.33
|
0.91
|
1.4
|
1.48
|
1.51
|
1.06
|
|
Tensile Strength at Yeild
|
D-638
ISO 527-2 |
psi
|
27,000
|
14,000
|
.
|
16,1000
|
17,000
|
.
|
14,000
|
13,500
|
24,000
|
13,000
|
|
Tensil Strenght
at Break |
D-638
ISO 527-2 |
psi
|
.
|
.
|
.
|
.
|
.
|
11,500
|
.
|
.
|
.
|
.
|
|
Elongation
at Break |
D-638
ISO 527-2 |
%
|
10
|
10 |
,
|
,
|
6
|
3
|
5
|
8
|
3
|
15
|
|
Flexural Strength
at Yeild |
D-790
ISO 178 |
psi
|
.
|
.
|
.
|
21,000
|
22,000
|
18,5000
|
23,000
|
,
|
,
|
18,500
|
|
Flexural
Modulus |
D-790
ISO 178 |
psi
|
1,750,000
|
300,000
|
349,500
|
550,000
|
900,000
|
715,000
|
900,000
|
725,000
|
1,360,000
|
457.000
|
|
Izod, Notched, R.T.
|
D-256
ISO 180 |
ft-lb/in
|
3.5
|
2.3
|
.
|
3.7
|
3
|
0.7
|
0.8
|
1
|
2
|
1.5
|
|
Flammability
|
FMVSS 302
|
in/min
|
<4
|
<4
|
.
|
.
|
.
|
.
|
HB
|
<4
|
HB
|
<4
|
|
Linear Mold
Shrinkage |
D-955
|
in/in
|
.002-.003
|
,
|
,
|
0.008
|
..
|
..
|
.003-.005
|
.
|
.003-.005
|
0.007
|
|
All grades of nylon can be:
HS - Heat Stalized L - Lubricated |
||||||||||||