PC ALLOYS (Polycarbonate)
|
|||||||||||
|
REINFORCED
|
POLYCARBONATE ALLOYS
|
||||||||||
|
Grade
|
PCR-1G20
|
PCR-1G30
|
PCR-1G40
|
PCR-1G60
|
PCR-1TF30
|
PCA 1103
|
CBT-1303
|
CBT-1314
|
CBT-1G20
|
||
|
Property
|
Test
Method |
Measure
|
10% Fiberglass
Reinforced |
15% Fiberglass
Reinforced |
20% Fiberglass
Reinforced |
30% Fiberglass
Reinforced |
13 % Teflon
Reinforced |
PC/ABS Alloy
|
PC/PBT Alloy
|
PC/PBT Alloy
|
10% Fiberglass
Reinforced PC/ABS Alloy |
|
Melt Flow
|
D-1238
ISO 1133 |
g/10 min
|
10
|
11
|
10
|
8
|
26.4
|
3
|
3
|
9
|
3
|
|
Density
|
D-792
ISO 1183 |
g/cm3
|
1.25
|
1.3
|
1.34
|
1.43
|
1.28
|
1.13
|
1.21
|
1.21
|
1.3
|
|
Tensile Strength
at Yeildt |
D-638
ISO 527-2 |
psi
|
9,500
|
11,250
|
16,000
|
18,000
|
7,579
|
7,700
|
8,000
|
8,000
|
9,000
|
|
Tensile Strength
at Break |
D-638
ISO 527-2 |
psi
|
,
|
,
|
,
|
,
|
,
|
,
|
,
|
,
|
,
|
|
Elongation At
Break |
D-638
ISO 527-2 |
%
|
15
|
11.5
|
8
|
4
|
39.6
|
.
|
100
|
100
|
5
|
|
Flexural Strength at
Yeild
|
D-790
ISO 178 |
psi
|
15
|
11.5
|
8
|
4
|
12,210
|
.
|
100
|
100
|
5
|
|
Flexural
Modulas |
D-790
ISO 178 |
psi
|
480,000
|
480,000
|
750,000
|
1,100,000
|
321,100
|
400,000
|
300,000
|
300,000
|
300,000
|
|
Izod, Notched, R.T.
|
D-256
ISO 180 |
ft-lb/in
|
2.2
|
2.1
|
2
|
2
|
14
|
10
|
15
|
15
|
3.6
|
|
Gardner Impact
|
D-5420
|
in/lbs
|
.
|
.
|
.
|
.
|
.
|
.
|
.
|
.
|
.
|
|
Flammability
|
FMVSS 302
|
in/min
|
<4
|
<4
|
<4
|
<4
|
.
|
<4
|
<4
|
.
|
<4
|
|
Linear Mold
Shrinkage |
D-955
|
in/in
|
0.003
|
0.002
|
0.002
|
0.002
|
0.006
|
0.007
|
.
|
0.007
|
.
|