PBT
|
||||||||||
| .. |
PBT BASED
|
PET BASED
|
||||||||
|
Grade
|
PBT 325
|
PBT 780
|
PBR-1G30
|
PBR-1G60
|
PBR2G30
|
PBR-1G61 SEO
|
PETR-1G60
|
PETR-1G3M35
|
||
|
Property
|
Test Method
|
Measure
|
General
Purpose |
General
Purpose |
15% Fiberglass
Reinforced |
30% Fiberglass
Reinforced |
15% Fiberglass
Reinforced |
Flame Retardant
30% Fiberglass Reinforced |
30% Fiberglass
Reinforced |
35% Gls fiber/Mineral
Reinforced Low Warp |
|
Melt Flow
|
D-1238
ISO 1133 |
g/10 min
|
.
|
22
|
.
|
.
|
.
|
6
|
,
|
.
|
|
Izod, Notched, R.T.
|
D-256
ISO 180 |
ft-lb/in
|
0.9
|
0.8
|
1
|
1.5
|
2
|
1.2
|
.
|
1.5
|
|
Melt Point
|
D-789
|
Deg F
|
,
|
.
|
.
|
442
|
442
|
,
|
,
|
482
|
|
Density
|
D792
ISO 1183 |
g/cm3
|
1.25
|
1.20
|
1.41
|
1.54
|
1.42
|
1.62
|
1.56
|
1.58
|
|
Tensil Strenth
at Yeild |
D-638
ISO 527-2 |
psi
|
7,300
|
8,100
|
.
|
15,000
|
10,000
|
.
|
21,000
|
17,000
|
|
Tensile Strenght
at Break |
D-638
ISO 527-2 |
psi
|
6,500
|
.
|
.
|
.
|
.
|
.
|
.
|
.
|
|
Elongation
at Break |
D-638
ISO 527-2 |
%
|
19
|
.
|
.
|
3
|
5
|
.
|
5
|
3
|
|
Flexural Strength
at Yeild |
D-790
ISO 178 |
psi
|
11,500
|
.
|
21,000
|
,
|
,
|
24,000
|
32,000
|
.
|
|
Flexural
Modulus |
D-790
ISO 178 |
psi
|
340,000
|
.
|
700,000
|
1,000,000
|
600,000
|
1,050,000
|
1,400,000
|
1,600,000
|
|
Flammability
|
FMVSS302
|
in/min
|
.
|
.
|
.
|
.
|
<4
|
,
|
,
|
<4
|
|
Linear Mold
Shrinkage |
D-955
|
in/in
|
.
|
.011-.022
|
,
|
0.003
|
0.005
|
0.004
|
0.0025
|
0.003
|