POLYPHENYLENE OXIDE
|
|||||||||
|
Grade
|
PPO 844
|
PPO 888
|
PPO 501-FRO
|
PPO FR1-701
|
PPO FRIG21
|
PPO FR1G41
|
PPo/PA 310
|
||
|
Property
|
Test
Method |
Measure
|
.
|
.
|
Flame Resistant
|
Flame Resistant
|
Flame Resistant
10% Fiberglass Reinforced |
Flame Resistant
20% Fiberglass Reinforced |
PPO/Polymide
Alloy |
|
Tensile Strength
at Yeild |
D-638
ISO 527-2 |
psi
|
7,500
|
8,000
|
7,000
|
9,200
|
10,000
|
15,000
|
8,500
|
|
Tensile Strength
at Break |
D-638
ISO 527-2 |
psi
|
.
|
.
|
.
|
.
|
.
|
.
|
.
|
|
Elongation
at Break |
D-638
ISO 527-2 |
%
|
40
|
30
|
60
|
50
|
.
|
.
|
.
|
|
Flexural Strength
at Yeild |
D-790
ISO 178 |
psi
|
10,000
|
12,000
|
11,500
|
14,200
|
17,000
|
20,000
|
113,000
|
|
Flexural Modulas
|
D-790
ISO 178 |
psi
|
350,000
|
370,000
|
360.000
|
375,000
|
500,000
|
800,000
|
325,000
|
|
Izod, Notched, R.T.
|
D-256
ISO 180 |
ft-lb/in
|
4
|
3.5
|
6
|
4.5
|
1.8
|
2
|
3.5
|
|
Flammability
|
FMVSS 302
|
in/min
|
<4
|
<4
|
V-2
|
V-0
|
V-1
|
V-1
|
.
|
|
Linear Mold
Shrinkage |
D-955
|
in/in
|
0.006
|
0.006
|
0.006
|
0.006
|
.003-.005
|
.002-.004
|
.012-.016
|
|
D.T.U.L.@66 psi
D.T.U.L. @ 264 psi |
D-648
|
Deg.F
|
230 |
240 |
190 |
253 |
269 |
266
275 |
375
285 |
|
Density
|
D-792
ISO 1183 |
g/cm3
|
1.06
|
1.04
|
1.08
|
1.06
|
1.16
|
1.23
|
1.1
|